# CORUS
# This file is automatically generated by Aurora of Corus Group plc.
# Corus has taken care to ensure that this information is accurate,
# but Corus Group plc including its subsidiaries does not accept responsibility or
# liability for errors or information which is found to be misleading.

# This material data is to be used for FE simulations only. Within the 
# natural spread of material properties, it gives typical values.
# These values cannot be used as reference for commercial issues.
# This material data is confidential, intended only for use of the individual or
# entity named below, and must not be distributed further.

# This file is made as input for R2R Forming - Autoform v4.1 - Hill'48.
# Autoform input deck: 2. Average in forming window - units: mm, N

# Serialnumber: R2R 200809220023
# Contact: AUTOMOTIVE BY CORUS
# Created by: Scholting, Marc
# Created on: 22-Sep-2008

# Grade: HCT600X
# Coating: +Z
# Thickness class: 1.2 <= t < 1.6

Youngs 210000 
Poisson 0.3 
SpecificWeight 7.8e-05 

## Hardening                                                          
## Method: Bergstrom fit of tensile test data from the Corus Works.

Hardening 
 0	0	385.24
 1	0.0036	413.78
 2	0.0079	442.29
 3	0.0128	470.72
 4	0.0186	499.06
 5	0.0252	527.32
 6	0.033	555.45
 7	0.0422	583.43
 8	0.0532	611.22
 9	0.0668	638.75
 10	0.0842	665.89
 11	0.1078	692.45
 12	0.1425	718.03
 13	0.2006	742.22
 14	0.3	764.52
 15	0.32	768.13
 16	0.34	771.66
 17	0.36	775.16
 18	0.38	778.67
 19	0.4	782.2
 20	0.42	785.78
 21	0.44	789.42
 22	0.46	793.11
 23	0.48	796.88
 24	0.5	800.71
 25	0.52	804.62
 26	0.54	808.59
 27	0.56	812.62
 28	0.58	816.67
 29	0.6	820.72
 30	0.62	824.77
 31	0.64	828.81
 32	0.66	832.86
 33	0.68	836.9
 34	0.7	840.94
 35	0.72	844.99
 36	0.74	849.03
 37	0.76	853.07
 38	0.78	857.11
 39	0.8	861.16
 40	0.82	865.2
 41	0.84	869.24
 42	0.86	873.28
 43	0.88	877.32
 44	0.9	881.37
 45	0.92	885.41
 46	0.94	889.45
 47	0.96	893.49
 48	0.98	897.53
 49	1	901.58
R-Values 0.918	0.851	1.063	
	
BiaxialStressFactor 1 

## Forming Limit Curve (FLC): Aurora databse 1.2 <= t < 1.6
## Method:  Based on set of Nakazima-type experimental FLCs.

Failure
 0	-0.12	0.4580644618044635	
 1	-0.09	0.38856807492539147	
 2	-0.06	0.32926298780342916	
 3	-0.03	0.27751070920046705	
 4	0	0.23115521676720646	
 5	0.03	0.19661089687245758	
 6	0.06	0.1948340156300704	
 7	0.09	0.21781963256878944	
 8	0.12	0.2421237575866128	
 9	0.15	0.2634037130326746	
 10	0.18	0.2828731271271654	
 11	0.21	0.30131084317964013	
 12	0.24	0.3189864850790962	
 13	0.27	0.335978747232546	
 14	0.3	0.35230888511529146	
 15	0.33	0.3679823900518979	
 16	0.36	0.38300064004567047	
 17	0.39	0.3973639738645963